Waterproof Styrene-Acrylic Emulsion Rg-T20019s

• Customization: Available
• Appearance: Liquid
• Usage: Coating Auxiliary Agents, Textile Auxiliary Agents, Leather Auxiliary Agents
• Model NO.: RG-T20019S
• Color: Milk White
• Ionicity: Anionic
• pH: 8.0-9.0
• Solid Content: 46%
• Viscosity: 200-1000
• Gtt: 25 Degree
• Mfft: 20 Degree
• Particel Dia.: 0.1-0.3 Um
• Transport Package: Plastic Drum
• Specification: 25kg, 50kg, 160kg
• Trademark: RG
• Origin: Weifang
• HS Code: 3906909000
• Production Capacity: 50000mt/Year

Product Description

Cross-linking agent RG-T20019S

Main ingredient: Styrene-acrylate copolymer

Physical/ chemical indicators:
Appearance: White with blue emulsion 
Iconicity: Anionic
P H: 8.0-9.0
Solid: 46.0%±1%
Viscosity: 200-1000(cps)(Brookfield LVT #3 @ 60rpm/25ºC)
GTT: Approximately 25ºC
MFFT: <20ºC
Partial size: 0.1-0.3μm

Characteristics and applications:
RG-T20019S is water and alkali resistance and good compatibility with cement. It is especially suitable to manufacture soft, water-resistant one-component mortars, suitable for crack filling materials and roof waterproof coatings. The finished product can be stored for six months.

Packaging and stored:
Packed in 50kg plastic drum or 200kg iron drum
Please store or transport this product in sealed container above 5ºC, avoid high temperature, direct sunlight and freeze.
Shelf life: 6 months
This product is water-based, non-toxic, non-hazardous. It is only suitable for industrial use. For details, please refer to the material safety sheet of the product.                    

Recommended Formula

1,Mix proportion:
Item			Weight(KG)
Cross-linking agent RG-T20019S			200
Dispersing agent WS-2650A			2.5
Wetting agent OP-10			1
Coalescing agents(TEXANOL)			0.6
Defoamer			4
TSP(400 mash)			100
TSP(800 mash)			100
DBP			20
1, Physical properties (according to JC/ t894-2001)
No.	Test item		I level standard	Test result
1	Solid,%		≥65	70
2	Drying time	Surface drying time (h)	≤4	3.6
		Hard drying time (h)	≤8	7.1
3	Tensile strength, no treatment(MPa)		≥1.0	1.1
4	Elongation at break, no treatment(%)		≥300	320
5	Low temperature flexible, Φ 10 bar		-10ºC,flawless	Flawless
6	Water tightness,0.3Mpa,30min		Waterproof	Waterproof