Waterproof Styrene Acrylate Emulsion Rg-T20020s

• Appearance: Liquid
• Usage: Coating Auxiliary Agents, Textile Auxiliary Agents, Leather Auxiliary Agents
• Color: Milk White
• Iconicity: Anionic
• pH: 8.0-10.0
• Solid Content: 54-57%
• Model NO.: RG-T20020S
• Viscosity: 400-1600(Cps)
• Gtt: Approximately -8 Degree
• Mfft: <0 Degree
• Partial Size: 0.2-0.4um
• Transport Package: Plastic Drum
• Specification: 25kg, 50kg, 160kg
• Trademark: RG
• Origin: Weifang
• HS Code: 3906909000
• Production Capacity: 50000mt/Year

Product Description

Cross-linking agent RG-T20020S

Main ingredient: Styrene-acrylate copolymer

Physical/ chemical indicators:
Appearance: White emulsion           
Iconicity: Anionic
P H: 8.0-10.0
Solid: 54-57%
Viscosity: 400-1600(cps)(Brookfield LVT #3 @ 60rpm/25ºC)
GTT: Approximately -8ºC
MFFT: <0ºC
Partial size: 0.2-0.4μm

Characteristics and applications:
RG-T20020S is water and alkali resistance and good compatibility with cement. It is especially suitable to manufacture soft, water-resistant two-component mortars, suitable for crack filling materials and roof waterproof coatings and ceramic tile adhesives.

Packaging and stored:
Packed in 50kg plastic drum or 200kg iron drum
Please store or transport this product in sealed container above 5ºC, avoid high temperature, direct sunlight and freeze.
Shelf life: 6 months
This product is water-based, non-toxic, non-hazardous. It is only suitable for industrial use. For details, please refer to the material safety sheet of the product.                    

Recommended Formula 1:1.2

1,Mix proportion:
Item				Weight(KG)
Liquid material		Cross-linking agent RG-T20020S		100
		Defoamer		1
		DBP		4
Power material		White cement 425#		41
		TSP(800 mash)		82
		Quartz powder(800 mash)		2.5
		Water reducer		0.5
1, Physical properties (according to JC/ t894-2001)
No.	Test item			I level standard	Test result
1	Solid,%			≥65	76
2	Drying time		Surface drying time (h)	≤4	3.3
			Hard drying time (h)	≤8	7
3	Tensile strength, no treatment(MPa)			≥1.2	1.74
4	Elongation at break, no treatment(%)			≥200	245
5	Low temperature flexible, Φ 10 bar			-10ºC,flawless	Flawless
6	Water tightness,0.3Mpa,30min			Waterproof	Waterproof

Recommended Formula 1:1.5

1,Mix proportion:
Item				Weight(KG)
Liquid material		Cross-linking agent RG-T20020S		100
		Defoamer		1
		DBP		4
Power material		White cement 425#		50
		TSP(400 mash)		51
		TSP(800 mash)		52
		Quartz powder(800 mash)		4
		Water reducer UNF		0.5
1, Physical properties (according to JC/ t894-2001)
No.	Test item			I level standard	Test result
1	Solid,%			≥65	79
2	Drying time		Surface drying time (h)	≤4	3
			Hard drying time (h)	≤8	6.8
3	Tensile strength, no treatment(MPa)			≥1.8	2.35
4	Elongation at break, no treatment(%)			≥80	135.4
5	Low temperature flexible, Φ 10 bar			-10ºC,flawless	Flawless
6	Water tightness,0.3Mpa,30min			Waterproof	Waterproof